Anti-crack Tape

Home Product Center Composite Material Anti-crack Tape

Anti-crack Tape

Fiber Reinforced High Toughness Waterproofing Anti-crack Patch is made from modified asphalt as the base material and high-performance composite basalt fibers as the substrate, produced through a high-temperature melting cycle. It exhibits excellent self-adhesion, high strength, and good impermeability and crack resistance.

High heat resistance
Reduced maintenance costs
High tensile intensity
Good self-adhesive effect

Product Advantages

Good self-adhesion and strong bonding with the roadbed and pavement
High tensile strength, along with low oil permeability, high heat resistance, and dimensional stability at high temperatures, which improves the bonding and impermeability of asphalt pavement interlayers, effectively preventing reflective cracks, water damage, and other issues
Waterproof, corrosion-resistant, and extends the service life of the road after maintenance
Convenient construction, reducing maintenance costs

Technical Parameters

Parameters			Technical Requirements
Thickness (mm)			≥ 2.0
Unit Area Mass (kg/m²)			≥ 2.0
Tensile Performance	Maximum Tensile Strength (N/50mm)	Longitudinal/Transverse	≥ 1400
Tensile Performance	Maximum Elongation at Maximum Tensile Strength (%)	Longitudinal/Transverse	1.0 - 10.0
Thermal Aging	Maximum Tensile Strength (N/50mm)	Longitudinal/Transverse	≥ 70.0
	Maximum Elongation at Maximum Tensile Strength (%)	Longitudinal/Transverse	≥ 75.0
	Mass Loss Rate (%)		士 2.0
	Dimensional Change Rate (%)		士 2.0
Low-Temperature Flexibility (-10°C)			No Cracking
Waterproofness (30 min, 0.3 MPa)			Waterproof